Thin film transistor and semiconductor device and method for forming the same

ABSTRACT

A thin film transistor and a semiconductor device and a method for forming the same. A silicon thin film formed on an insulating substrate is heated at 550 to 800° C. so that it has crystallinity, and a thin film transistor is formed using the crystalline silicon film thus obtained. Thermal contraction of the insulating substrate is set in a range of 30 to 500 ppm in the heating process, so that the thin film transistor has high mobility, low threshold voltage and high off-resistance. Thermal contraction of the insulating substrate may be also set 100 ppm or less in a heating process after a patterning treatment in a thin film transistor producing process.

This application is a Continuation of Ser. No. 08/191,709, filed Feb. 4, 1994, now abandoned; which itself is a division of Ser. No. 07/856,643, filed Mar. 24, 1992, abandoned.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a thin film transistor and a semiconductor device and a method for forming the same, more particularly to a method of producing a silicon thin film transistor for use in an active matrix drive type liquid crystal display, an image sensor, a thermal head, etc., and to a silicon thin film transistor manufactured by the same.

2. Description of Prior Art

A silicon thin film transistor has been hitherto utilized in a liquid crystal display for a compact TV or computer, and an active element or a part of a drive circuit for an image sensor and a thermal head which are used in a facsimile machine, etc. An amorphous silicon thin film transistor is being most vigorously developed now because it can be manufactured relatively easily and designed in a large area.

The amorphous silicon thin film transistor, however, has a demerit that electron and hole mobilities are very small, 1 cm² /Vsec and 0.1 cm² /Vsec respectively. This is not a critical problem, for example when it is used to perform a switching operation of each pixel of a liquid crystal display or each bit of an image sensor, but is a critical problem particularly in a switching speed when a drive circuit is constructed the same on substrate.

On the other hand, a polycrystal silicon thin film transistor which has been used for a compact-size liquid crystal TV or an image sensor has electron and hole mobilities of about 10 cm² /Vsec, and some driving circuits comprising polycrystal silicon thin film transistors are actually marketed as a product. However, the polycrystal silicon thin film transistor is also insufficient to satisfy scale-up and speed-up needs of a device. The polycrystal silicon thin film transistor has polycrystal silicon film formed in an active layer by an LPCVD method, for example. Such polycrystal silicon has a high potential barrier at a grain boundary, so that both of electron and hole mobilities are limited to about 10 cm² /Vsec or less. In addition, in most cases, cost is high because of use of expensive quartz as a substrate.

Apart from such amorphous silicon thin film transistor or polycrystal silicon thin film transistor, another method in which amorphous silicon film is formed on a substrate formed of quartz or glass, and then heated for a long time to be grown in solid phase and crystallized has been recently studied. This method provides a thin film transistor having a high mobility of several times to several-tens times of that of a polycrystal silicon thin film transistor (this is dependent on a process condition), and also has high productivity, so that this method is more effective for the next generation's active matrix drive liquid crystal display having driving circuits formed on the same large substrate, for example.

Since a quartz substrate is durable to high temperature above 1000° C., the following advantages are obtained: a gate insulation film formed by thermal oxidation of silicon active layer, which is used generally in silicon wafer process, can be adopted, and a quartz substrate provides a good silicon/silicon-oxide interface. However, the thin film transistor grown in solid phase on the quartz substrate by above method has not only a problem that stable and uniform characteristics cannot be obtained because of lack of uniformity of thermal contraction of quartz, but also a problem that there occurs a failure due to an instability phenomenon that reduction of off resistance and current-curve variation with time lapse are developed, and these problems make it difficult to realize large-area device. In addition, the quartz substrate is more expensive several times than glass, especially for a large-area substrate, so that the quartz would be unsuitable as substrate in this respect.

On the other hand, relatively-low cost glass which is durable to a thermal process of about 600° C. at maximum has been recently developed. Some kinds of this glass can be used for a solid-phase thermal growth process below 600° C. because they contain a small amount of alkali component. These kinds of glass show a very large coefficient of thermal contraction by heating them at 600° C. for 24 hours, for example. Therefore, when a thin film transistor is formed on such a glass substrate, a threshold voltage is observed to be shifted to a positive side by 2 to 5 volt because the substrate is thermally contracted by a heat-treatment in a crystallization process of the semiconductor film, so that a compression stress acts on an active layer of the thin film transistor and the interface condition of the active layer silicon/gate insulator layer is deteriorated.

In addition, since the thermal contraction of the substrate exceeds 200 ppm in a heating process for activating impurities doped in the thin film transistor, a pattern alignment is difficult even using a reduction projecting light exposure device having a mechanism of correcting a substrate expansion and contraction, especially when the diagonal length of the substrate exceeds 10 inches.

SUMMARY OF THE INVENTION

An object of this invention is to provide a method for forming on an insulating substrate a crystalline amorphous silicon thin film transistor in which high carrier mobility, low threshold voltage and high off-resistance can be stably obtained.

In order to attain the above and other objects, the method according to this invention is a method for changing a silicon thin film formed on an insulating substrate to a silicon thin film having crystallinity by a thermal process of 550 to 800° C. to produce a thin film transistor using a crystalline silicon thin film, wherein thermal contraction of the insulating substrate by the thermal process is controlled to be 30 to 500 ppm (parts per million), preferably 30 to 200 ppm to make film quality of the silicon thin film excellent, thereby stably producing a thin film transistor having high mobility, low threshold voltage and high off-resistance.

According to this invention, on a way of a thin film transistor forming process, a pattern is formed on the insulating substrate and the pattern formed on the insulating substrate is subjected to thermal treatment with thermal contraction of said insulating substrate being controlled to be 100 ppm or less.

In order to restrict the thermal contraction of the substrate to the above range, the insulating substrate is thermally treated at 550 to 800° C. before the silicon thin film is formed on the substrate.

By adopting the producing method of the thin film transistor mentioned above, mobilities of electron and hole exceed 80 cm² /Vsec and 50 cm² /Vsec respectively, and the absolute value of a threshold voltage of NMOS and PMOS can be stabilized under 6 volts.

In addition, a thin film transistor in which an off-resistance of 1 GΩ or more could be obtained for |V_(DS) |=5 V and V_(G) =0 V could be produced without a special structure of transistor.

Further, since thermal contraction of the insulating substrate was suppressed below 100 ppm by the thermal treatment of the insulating substrate in the manner as described above, and thus the patterning can be carried out with a low-price contact-type light exposure device or a proximity light exposure device.

There has been conventionally a technical idea that the thermal contraction should be suppressed to the utmost or that the degree of the thermal contraction of the semiconductor itself is coincident with that of the thermal contraction of the substrate. However, this invention differs from the above conventional technical idea, and has a novel technical idea that a compression stress is applied to the semiconductor film to the extent that characteristics of the semiconductor film are not deteriorated, thereby obtaining a thin film transistor having good semiconductor characteristics, high mobility, low threshold voltage and high off-resistance.

That is, the compression stress is slightly applied to the semiconductor film so that the thermal contraction of the substrate in a crystallization process is controlled to be above 30 ppm, and in order to prevent deterioration of the characteristics of the semiconductor film due to the excessive compression stress, the upper limit of the thermal contraction of the substrate is restricted to 500 ppm or less, preferably below 200 ppm, thereby realizing more excellent film characteristics.

Further, there is a problem in the thin film transistor forming process that if the substrate is contracted in a process after the patterning treatment, an alignment process cannot be carried out in a next process. Therefore, the thermal contraction of the substrate is set 200 ppm or less, preferably 100 ppm or less to perform the alignment process. Especially for the thermal contraction of 100 ppm or less, a contacting light-exposure type and a proximity light exposure type of an alignment device are usable, so that the thin film transistor can be produced with a low-cost device.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1(A)-1(F) are a longitudinal-sectional view of a producing process of a thin film transistor according to this invention;

FIGS. 2(A)-2(B) are a graph showing static characteristics of gate voltage--source/drain current of the thin film transistor according to this invention;

FIGS. 3(A)-3(B) are another graph of static characteristics of gate voltage--source/drain current of the thin film transistor according to this invention; and

FIGS. 4(A)-4(B) are a graph of static characteristics of gate voltage--source/drain current of a thin film transistor produced by a comparison example.

DETAILED DESCRIPTION OF THE INVENTION

Preferred embodiments will be described hereunder with reference to the accompanying drawings.

(EMBODIMENT 1)

FIG. 1 is a schematic diagram of a producing process of an embodiment of a thin film transistor of this invention. A glass substrate 100 was first annealed at 600° C. in a oven for a long time. A 48-hours annealing was enough when an used substrate was formed of crystallized glass, for example. At this time, the substrate was contracted by about 300 ppm. In order to prevent diffusion of impurities in the glass substrate, a silicon-oxide film 101 was formed in 1000 Å to 3000 Å by a sputtering method.

Next, amorphous silicon film 102 was formed in 1500 Å thickness by a low pressure CVD method or a plasma CVD method, and annealed at 600° C. for 48 hours and further at 800° C. for one hour successively, to crystallize the amorphous silicon. Thereafter, an ordinary producing process of a thin film transistor was carried out.

First, a crystallized silicon film was patterned in an islandish form as shown in FIG. 1(a). Next, a silicon oxide film 103 was formed as a gate insulating film in 1000 Å thickness by the sputtering method. The sputtering process was carried out in 100% oxygen atmosphere using a synthetic quartz as a sputtering target. Although the thin film transistor could be also produced using a silicon oxide film produced by an atmospheric pressure CVD method, a low pressure CVD method and a photo CVD method, it was found out that a silicon oxide film formed by the sputtering method had most excellent characteristics. Thereafter, an n⁺ -silicon layer 104 containing phosphorus or arsenic of about 1×10²¹ or more was formed by the low pressure CVD method or plasma CVD method, and then a gate electrode was formed by the patterning process as shown in FIG. 1(b).

At this state, boron of 1×10¹⁵ atoms/cm² was injected to the whole surface of the element as shown in FIG. 1(b) by an ion implantation method as shown in FIG. 1(c). Further, a region at which a PMOS would be formed was covered by a resist 105 or the like, and a region at which an NMOS would be formed was doped with phosphorus of 5×10¹⁵ atoms/cm² by the ion implantation as shown in FIG. 1(d). Source and drain semiconductor regions were then formed in the silicon film in the PMOS and the NMOS. The thermal contraction of the substrate was observed to be 10 ppm or less after an activation treatment at 600° C. for 24 hours, and thus there was no problem for a positioning of a photomask.

Thereafter, a silicon-oxide film of about 1 micron was formed as an interlayer insulating film 106 by the atmospheric pressure CVD method or sputtering method as shown in FIG. 1(e). After a contact hole was formed in the interlayer insulating film, Al electrode 107 was formed and the patterning process was carried out as shown in FIG. 1(f), the element thus formed was sintered at 375° C. to form the thin film transistor.

FIG. 2(a) and FIG. 2(b) show measured static characteristics of NMOS and PMOS respectively of a silicon thin film transistor which was produced by the method as described above. Ratios of channel-length/channel-width of NMOS and PMOS were 5 micron/21 micron, and 6 micron/35 micron respectively, and a measurement condition is listed in the figures. Both of the static characteristics showed good characteristics. A field effect mobility μFE was 81.5 cm² /Vsec and 55.2 cm² /Vsec respectively and a threshold voltage V_(th) is 3.2 V and -4.8 V, respectively.

(EMBODIMENT 2)

A thin film transistor was produced in the same process as the embodiment 1, except that the anneal process at 800° C. for an hour after the solid-phase growth in the annealing process at 600° C. for 48 hours was not carried out.

FIGS. 3(a) and (b) show static characteristics of the thin film transistor thus formed. Since the thermal contraction of the substrate after the activation treatment of an impurity region was about 30 ppm, there was no problem for the subsequent patterning process. Field effect nobilities of NMOS and PMOS were 57.7 cm² /Vsec and 36.3 cm² /Vsec, respectively, and threshold voltages thereof were 5.2 V and -5.7 V.

(COMPARISON EXAMPLE)

An example using a low alkali glass different from that of the embodiment 1 will be shown as a comparison example. First, a pre-anneal process was carried out at 600° C. for 48 hours, and a solid-phase growth was carried out by the annealing treatment at 600° C. for 48 hours. The subsequent processes were identical to those of the embodiment 1. In this process, the thermal contraction were measured to be 900 to 1000 ppm in the solid-phase growth process and 300 ppm in the activation process.

It was found from the measurement of the characteristics of the thin film transistor thus obtained that a threshold voltage is shifted to a positive gate voltage side by 3 to 4 volts for NMOS and by 2 to 3 volts for PMOS as shown in FIGS. 4(a) and (b). In addition, a phenomena that rise-up of a current value of the PMOS is sluggish was observed.

Further, in the processes, the mask alignment was very difficult because the thermal contraction of the substrate in the activation treatment process after the patterning process was excessively large, so that the thin film transistor could be formed on only a part of the substrate.

According to the thin film transistor producing method as described above, a thin film transistor having an electron mobility of 80 cm² /Vsec or more and a hole mobility of 50 cm² /Vsec or more can be obtained, and the absolute value of a threshold voltage of each of NMOS and PMOS can be stabilizingly set 6 volts or less. In addition, a thin film transistor in which an off-resistance of 1 GΩ or more could be obtained for |V_(DS) |=5 V and V_(G) =0 V could be produced without a special structure of transistor.

Further, the thermal contraction of the substrate in the heat treatment process after the patterning process can be restricted to a value below 100 ppm, so that the patterning process can be carried out using a low-price contact light exposure device or proximity light exposure device. 

What is claimed is:
 1. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of threshold voltage of 6 V or less and field effect mobility of 50 cm² /V sec or higher in the case of the p-channel transistor and 80 cm² /V sec or higher in the case of the n-channel transistor, said method comprising the steps of:preheating a glass substrate in order to contract said glass substrate; forming a semiconductor film comprising silicon over said glass substrate; crystallizing said semiconductor film by heating subsequent to said preheating by which said glass substrate contracts at 30-500 ppm; patterning said semiconductor film after said crystallizing into a plurality of semiconductor islands; forming a gate insulating layer and a gate electrode on said semiconductor islands; forming a pair of impurity regions in said semiconductor islands; and then activating said impurity regions, wherein a thermal contraction of said glass substrate is less than 100 ppm during the steps subsequent to said patterning through said activating step.
 2. The method of claim 1 wherein the step of preheating said glass substrate is conducted at 550-800° C.
 3. The method of claim 1 further comprising the step of forming a silicon oxide film on said glass substrate prior to forming said semiconductor film.
 4. The method of claim 1 wherein said semiconductor film is heated at 550-800° C. during said crystallizing.
 5. The method of claim 1 wherein said glass substrate comprises a crystallized glass.
 6. The method of claim 1 wherein said patterning is performed by using an aligner of a contact light exposure or a proximity light exposure.
 7. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of threshold voltage of 6 V or less and field effect mobility of 50 cm² /V sec or higher in the case of the p-channel transistor and 80 cm² /V sec or higher in the case of the n-channel transistor, said method comprising the steps of:preheating a glass substrate in order to contract said glass substrate; forming a semiconductor film comprising silicon over said glass substrate; crystallizing said semiconductor film by heating subsequent to said preheating by which said glass substrate contracts at 30-500 ppm; patterning said semiconductor film after said crystallizing into a plurality of semiconductor islands; forming a pair of impurity regions in said semiconductor islands and then activating said impurity regions, wherein a thermal contraction of said glass substrate is less than 100 ppm during the steps subsequent to said patterning through said activating step.
 8. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of threshold voltage of 6 V or less and field effect mobility of 50 cm² /V sec or higher in the case of the p-channel transistor and 80 cm² /V sec or higher in the case of the n-channel transistor, said method comprising the steps of:preheating a glass substrate in order to contract said glass substrate; forming a semiconductor film comprising silicon over said glass substrate; crystallizing said semiconductor film by heating subsequent to said preheating at a temperature of 550 to 800° C. by which said glass substrate contracts at 30-500 ppm; patterning said semiconductor film after said crystallizing into a plurality of semiconductor islands; forming a gate insulating layer and a gate electrode on said semiconductor islands; forming a pair of impurity regions in said semiconductor islands; and then activating said impurity regions, wherein a thermal contraction of said glass substrate is less than 100 ppm during the steps subsequent to said patterning through said activating step.
 9. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of threshold voltage of 6 V or less and field effect mobility of 50 cm² /V sec or higher in the case of the p-channel transistor and 80 cm² /V sec or higher in the case of the n-channel transistor, said method comprising the steps of:preparing a glass substrate which has been preheated in order to contract said glass substrate; forming a semiconductor film comprising silicon over said glass substrate; crystallizing said semiconductor film by heating subsequent to said preheating by which said glass substrate contracts at 30-500 ppm; patterning said semiconductor film after said crystallizing into a plurality of semiconductor islands; forming a gate insulating layer and a gate electrode on said semiconductor islands; forming a pair of impurity regions in said semiconductor islands and then activating said impurity regions, wherein a thermal contraction of said glass substrate is less than 100 ppm during the steps subsequent to said patterning through said activating step.
 10. The method of claim 9 further comprising the step of forming a silicon oxide film on said glass substrate prior to forming said semiconductor film.
 11. The method of claim 9 wherein said semiconductor film is heated at 550-800° C. during said crystallizing.
 12. The method of claim 9 wherein said glass substrate comprises a crystallized glass.
 13. The method of claim 9 wherein said patterning is performed by using an aligner of a contact light exposure or a proximity light exposure.
 14. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of threshold voltage of 6 V or less and field effect mobility of 50 cm² /V sec or higher in the case of the p-channel transistor and 80 cm² /V sec or higher in the case of the n-channel transistor, said method comprising the steps of:preparing a glass substrate which has been preheated in order to contract said glass substrate; forming a semiconductor film comprising silicon over said glass substrate; crystallizing said semiconductor film by heating subsequent to said preheating at a temperature 550 to 800° C. by which said glass substrate contracts at 30-500 ppm; patterning said semiconductor film after said crystallizing into a plurality of semiconductor islands; forming a pair of impurity regions in said semiconductor islands and then activating said impurity regions, wherein a thermal contraction of said glass substrate is less than 100 ppm during the steps subsequent to said patterning through said activating step.
 15. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of threshold voltage of 6 V or less and field effect mobility of 50 cm² /V sec or higher in the case of the p-channel transistor and 80 cm² /V sec or higher in the case of the n-channel transistor, said method comprising the steps of:preparing a glass substrate which has been preheated in order to contract said glass substrate; forming a semiconductor film comprising silicon over said glass substrate; crystallizing said semiconductor film by heating subsequent to said preheating at a temperature 550 to 800° C. by which said glass substrate contracts at 30-500 ppm; patterning said semiconductor film after said crystallizing into a plurality of semiconductor islands; forming a gate insulating layer and a gate electrode on said semiconductor islands; forming a pair of impurity regions in said semiconductor islands and then activating said impurity regions, wherein a thermal contraction of said glass substrate is less than 100 ppm during the steps subsequent to said patterning through said activating step.
 16. The method of claim 7 wherein said glass substrate comprises a crystallized glass.
 17. The method of claim 8 wherein said glass substrate comprises a crystallized glass.
 18. The method of claim 14 wherein said glass substrate comprises a crystallized glass.
 19. The method of claim 15 wherein said glass substrate comprises a crystallized glass.
 20. A method of manufacturing a p-channel or n-channel thin film transistor comprising the steps of:preparing a glass substrate which has been preheated in order to contract said glass substrate; forming an insulating film comprising silicon oxide on said glass substrate; forming a semiconductor film comprising silicon over said insulating film; crystallizing said semiconductor film by heating subsequent to said preheating by which said glass substrate contracts at 30-500 ppm; patterning said semiconductor film after said crystallizing step into at least one semiconductor island; forming a gate electrode adjacent to said semiconductor island with an insulating layer interposed therebetween; forming a pair of impurity regions in said semiconductor islands; and activating said impurity regions.
 21. The method of claim 20 wherein said p-channel or n-channel thin film transistor has an absolute value of threshold voltage of 6 V or less and field effect mobility of 50 cm² /V sec or higher in the case of the p-channel thin film transistor and 80 cm² /V sec or higher in the case of the n-channel thin film transistor.
 22. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of a threshold voltage 6 V or less and field effect mobility 50 cm² /Vsec or higher in the case of the p-channel type and 80 cm² /Vsec or higher in the case of the n-channel type, said method comprising the steps of:preheating-a glass substrate in order to contract said glass substrate; forming a film having a thickness of 1000 to 3000 Å on said glass substrate, wherein said film prevents diffusion of impurities in said glass substrate; forming a semiconductor film comprising silicon on said film; and crystallizing said semiconductor film by heating, wherein said glass substrate contracts at 30-500 ppm in said crystallizing.
 23. The method of claim 20 wherein said film comprises silicon oxide.
 24. The method of claim 20 wherein said glass substrate is heated at 550 to 800° C. in said preheating.
 25. The method of claim 24 wherein said glass substrate is heated at 600° C. for 48 hours in said preheating.
 26. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of a threshold voltage 6 V or less and field effect mobility 50 cm² /Vsec or higher in the case of the p-channel type and 80 cm² /Vsec or higher in the case of the n-channel type, said method comprising the steps of:preheating a glass substrate in order to contract said glass substrate; forming a film on said glass substrate, wherein said film prevents diffusion of impurities in said glass substrate; forming a semiconductor film comprising silicon on said film; and crystallizing said semiconductor film by heating, wherein said glass substrate contracts at 30-500 ppm in said crystallizing.
 27. The method of claim 26 wherein said film comprises silicon oxide.
 28. The method of claim 26 wherein said glass substrate is heated at 550 to 800° C. in said preheating.
 29. The method of claim 28 wherein said glass substrate is heated at 600° C. for 48 hours in said preheating.
 30. A method of manufacturing a p-channel or n-channel thin film transistor comprising the steps of:preheating a glass substrate in order to contract said glass substrate; forming a film on said glass substrate, wherein said film prevents diffusion of impurities in said glass substrate; forming a semiconductor film comprising silicon on said film; and crystallizing said semiconductor film by heating, wherein said glass substrate contracts at 30-500 ppm in said crystallizing.
 31. The method of claim 30 wherein said film comprises silicon oxide.
 32. The method of claim 30 wherein said glass substrate is heated at 550 to 800° C. in said preheating.
 33. The method of claim 32 wherein said glass substrate is heated at 600° C. for 48 hours in said preheating.
 34. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of a threshold voltage 6 V or less and field effect mobility 50 cm² /Vsec or higher in the case of the p-channel type and 80 cm² /Vsec or higher in the case of the n-channel type, said method comprising the steps of:preparing a glass substrate which has been preheated in order to contract said glass substrate; forming a film having a thickness of 1000 to 3000 Å on said glass substrate, wherein said film prevents diffusion of impurities in said glass substrate; forming a semiconductor film comprising silicon on said film; and crystallizing said semiconductor film by heating, wherein said glass substrate contracts at 30-500 ppm in said crystallizing.
 35. The method of claim 34 wherein said film comprises silicon oxide.
 36. The method of claim 34 wherein said glass substrate has been preheated at 550 to 800° C.
 37. The method of claim 32 wherein said glass substrate has been preheated at 600° C. for 48 hours.
 38. A method for manufacturing a p-channel or n-channel thin film transistor, said transistor having an absolute value of a threshold voltage 6 V or less and field effect mobility 50 cm² /Vsec or higher in the case of the p-channel type and 80 cm² /Vsec or higher in the case of the n-channel type, said method comprising the steps of:preparing a glass substrate which has been preheated in order to contract said glass substrate; forming a film on said glass substrate, wherein said film prevents diffusion of impurities in said glass substrate; forming a semiconductor film comprising silicon on said film; and crystallizing said semiconductor film by heating, wherein said glass substrate contracts at 30-500 ppm in said crystallizing.
 39. The method of claim 38 wherein said film comprises silicon oxide.
 40. The method of claim 38 wherein said glass substrate has been preheated at 550 to 800° C.
 41. The method of claim 40 wherein said glass substrate has been preheated at 600° C. for 48 hours.
 42. A method for manufacturing a p-channel or n-channel thin film transistor comprising the steps of:preparing a glass substrate which has been preheated in order to contract said glass substrate; forming a film on said glass substrate, wherein said film prevents diffusion of impurities in said glass substrate; forming a semiconductor film comprising silicon on said film; and crystallizing said semiconductor film by heating, wherein said glass substrate contracts at 30-500 ppm in said crystallizing.
 43. The method of claim 42 wherein said film comprises silicon oxide.
 44. The method of claim 42 wherein said glass substrate has been preheated at 550 to 800° C.
 45. The method of claim 44 wherein said glass substrate has been preheated at 600° C. for 48 hours. 